NMX-J-191
Heat Deformation of Semiconductive Shielding, Insulations and Protective Coverings of Electrical
Conductors – Test Method
5.1.3 Deformation
5.1.3.1 Insulation
The insulation on single-conductor wires, and on the individual conductors (separated, in the case of
parallel cords), shall not decrease by more than 50% in thickness when subjected to a force caused by a
mass as shown in Table 40, and while maintained at the temperature shown in Table 40 for 1 h.
5.1.3.2 Jacket
Smoothed specimens of jackets from finished cords and cables shall not decrease by more than 50% in
thickness when subjected to a force caused by a mass of 2000 g, and while maintained at the temperature
shown in Table 40 for 1 h.
5.1.3.3 Method
Compliance with Clauses 5.1.3.1 and 5.1.3.2 shall be determined in accordance with the method
described in CSA C22.2 No. 0.3, Clause 4.3.6.1; UL 1581, Section 560; or NMX-J-191-ANCE.
UL62里有要求做此测试的电线型号里,没有SVOO的型号!
ul测试里,哑铃片的厚度是用什么仪器,什么方法测试的?哪位大侠知道啊?还有断裂点是在什么位置才算是有效的啊?
照常理,测试绝缘电阻是15M的,如果客户需要用20M去做测试,你可以将相关标准提供给客户,与客户沟通.
哑铃片的厚度是可以在成大片的时候定的,是压片机,不知道你们有没有用过,另外压片机压完后可以用卡尺量一下.
哑铃片的的断是要在中间夹的位置就视为合格,并且在压哑铃片时不能有毛边,也就是说压的时候用力点,呵呵,只要做过这些的就应该有心得了.
可是有的试验室用的是光显测微仪来测试厚度的,但是那样测试的话就应该是破坏性的测试,那么他的测试数据是怎么和哑铃片的实际数据统一的呢?另外你说的压片机应该是在做小样的时候才那样处理的!成品测试是不可能用到的是吗?谢谢回复!
经验啊！学习了
光显测微仪来测试厚度用得很少,因为测量厚度正常测试用的是卡尺,千分尺,测厚规,还有就是投影仪了,并且做成哑铃片的多为PVC或其它胶料类的,用光显测微仪来测试厚度的我还是很少听到,正常应该是用投影仪,但在用投影仪时如果不切开的话也比较难做到,除非他们有专门的固定治具;还有另类的哑铃片是可以开模具成型的,不知道你们有没有做过,开模具成型的其实也是有一道理的,就看贵司的实际情况了!
打啞鈴要做到不毛邊是有難度的，一般都會出現
UL工程師說測厚度其用的是Microscope ，到底怎麼理解這個詞呢?愚昧啊!!
呵呵,如果用模具成型是不会有毛边的...
另外测试哑铃片用的应该是投影仪,或者千分尺!
应该一般来说最常用的是1.6mm的还有3.2mm的
引用第27楼jackpan于2007-08-09 20:30发表的:
呵呵,如果用模具成型是不会有毛边的...
另外测试哑铃片用的应该是投影仪,或者千分尺!
投影仪和千分尺测试哑铃片的厚度?准确吗?